| | Nickel Chemical Properties |
| Melting point | 1453 °C (lit.) | | Boiling point | 2732 °C (lit.) | | density | 8.9 g/mL at 25 °C (lit.) | | vapor density | 5.8 (vs air) | | storage temp. | no restrictions. | | form | wire | | Specific Gravity | 8.9 | | color | White to gray-white | | PH | 8.5-12.0 | | Odor | Odorless | | PH Range | 9 - 11 at 20 °C | | resistivity | 6.97 μΩ-cm, 20°C | | Water Solubility | It is insoluble in water. | | Sensitive | air sensitive | | Merck | 14,8107 | | Exposure limits | TLA-TWA (metal) 1 mg/m3 (ACGIH,
MSHA, and OSHA); (soluble inorganic compounds)
0.1 mg(Ni)/m3 (ACGIH) 0.015 mg
(Ni)/m3 (NIOSH); (insoluble inorganic compounds)
1 mg/m3 (ACGIH). | | Stability: | Stable in massive form. Powder is pyrophoric - can ignite spontaneously. May react violently with titanium, ammonium nitrate, potassium perchlorate, hydrazoic acid. Incompatible with acids, oxidizing agents, sulfur. | | InChIKey | PXHVJJICTQNCMI-UHFFFAOYSA-N | | CAS DataBase Reference | 7440-02-0(CAS DataBase Reference) | | IARC | 2B (Vol. Sup 7, 49) 1990 | | NIST Chemistry Reference | Nickel(7440-02-0) | | EPA Substance Registry System | Nickel (7440-02-0) |
| Hazard Codes | C,Xi,Xn,F,T | | Risk Statements | 34-50/53-43-40-10-17-52/53-48/23 | | Safety Statements | 26-45-60-61-36-22-36/37-16-15-5-36/37/39-43-28 | | RIDADR | UN 1493 5.1/PG 2 | | WGK Germany | 3 | | RTECS | VW4725000 | | F | 8 | | Autoignition Temperature | 87 °C | | TSCA | Yes | | HazardClass | 4.1 | | PackingGroup | II | | HS Code | 38151100 | | Hazardous Substances Data | 7440-02-0(Hazardous Substances Data) | | Toxicity | Occupational exposures
may occur in its mining, smelting, and refining. The general
population ingests nickel in food. Skin sensitization and
dermatitis leading to chronic eczema, called “nickel itch,”
frequently occurs, especially in wearers of pierced earrings.
Nickel can also irritate the conjunctiva and respiratory tract
mucous membranes. Absorption from the digestive tract is
poor, so systemic poisoning is rare, but since it is an irritant
it acts as an emetic. Systemic effects include hyperglycemia,
capillary damage, CNS depression, myocardial weakness, and
kidney damage. Nickel and its compounds are carcinogenic
following inhalation, but not following ingestion or skin contact. Cancer of the lung and nasal passages results, with a
latent period of about 25 years; smokers are at greater risk.
In addition to irritation and carcinogenesis, nickel carbonyl
(nickel tetracarbonyl, Ni(CO)4) exerts relatively mild, tran_x0002_sientinitial symptoms including headache, giddiness, nausea,
and shortness of breath. These symptoms are followed by
very serious symptoms hours to days later, consisting of tightness in the chest, shortness of breath, rapid respiration, pulmonary edema, cyanosis, and extreme weakness; this can be
fatal. Heat decomposition of nickel carbonyl yields carbon
monoxide. Chelating agents can be used to remove nickel
from the body. | | IDLA | 10 mg Ni/m3 |
| | Nickel Usage And Synthesis |
| History | Nickel was isolated first and recognized as an element by Cronstedt in 1751. The metal was derived in pure form by Richter in 1804. The metal takes its name from two German words ‘Nickel’ and ‘kupfernickel’, which mean Old Nick’s (or Satan) and Old Nick’s copper, respectively.
The abundance of nickel in the earth’s crust is only 84 mg/kg, the 24th most abundant element. It is found in most meteorites, particularly in the iron meteorites or siderites, alloyed with iron. Its average concentration in seawater is 0.56 μg/mL. Nickel is one of the major components of the earth’s core, comprising about 7%.
The most common nickel ores are pentlandite, (Ni,Fe)9S16, limonite, (Fe,Ni)O(OH)•nH2O, and garnierite, (Ni,Mg)6Si4O10(OH)8. Other ores that are of rare occurrence are the sulfide ores, millerite, NiS, polydymite Ni3S4 and siegenite, (Co,Ni)3S4; the arsenide ores niccolite, NiAs, gersdorffite, NiAsS, and annabergite, Ni3As2O8•8H2O; and the antimonide ore, NiSb.
| | Uses | The most important applications of nickel metal involve its use in numerous alloys. Such alloys are used to construct various equipment, reaction vessels, plumbing parts, missile, and aerospace components. Such nickel-based alloys include Monel, Inconel, Hastelloy, Nichrome, Duranickel, Udinet, Incoloy and many other alloys under various other trade names. The metal itself has some major uses. Nickel anodes are used for nickel plating of many base metals to enhance their resistance to corrosion. Nickel-plated metals are used in various equipment, machine parts, printing plates, and many household items such as scissors, keys, clips, pins, and decorative pieces. Nickel powder is used as porous electrodes in storage batteries and fuel cells.
Another major industrial use of nickel is in catalysis. Nickel and raney nickel are used in catalytic hydrogenation or dehydrogenation of organic compounds including olefins, fats, and oils.
| | Production | Nickel usually is recovered from its sulfide ore, pentlandite (Ni,Fe)9S16. Although laterite type oxide ores sometimes are used as starting materials, pentlandite is used in many commercial operations. Pentlandite often is found in nature associated with other sulfide minerals, such as pyrrhotite, Fe7S8,and chalcopyrite, CuFeS2.
The ores are crushed and powdered. Sulfides are separated from gangue by froth flotation or magnetic separation processes. After this, the ore is subjected to roasting and smelting. These steps are carried out initially in rotary kilns or multihearth furnaces and then smelting is done in either blast furnaces or reverberatory, or arc furnaces. Most sulfur is removed as sulfur dioxide. Iron and other oxides produced in roasting are also removed along with siliceous slag during smelting. A matte obtained after smelting usually contains impure nickel-iron-copper sulfides and sulfur. The molten matte is treated with silica and an air blower in a converter in the Bessemerizing stage to remove all remaining iron and sulfur.
Copper-nickel matte obtained in this stage is allowed to cool slowly over a few days to separate mineral crystals of copper sulfide, nickel sulfide and nickel-copper alloy. The cool matte is pulverized to isolate sulfides of nickel and copper by froth flotation. Nickel-copper alloy is extracted by magnetic separation. Nickel metal is obtained from the nickel sulfide by electrolysis using crude nickel sulfide cast into anodes and nickel-plated stainless steel cathodes.
Alternatively, nickel sulfide is roasted to nickel oxide, which then is reduced to crude nickel and is electrorefined as above.
Two other refining processes are also frequently employed. One involves hydrometallurgical refining in which sulfide concentrates are leached with ammonia solution to convert the copper, nickel, and cobalt sulfides into their complex amines. Copper is precipitated from this solution upon heating. Under such conditions, the sulfide-amine mixture of nickel and cobalt are oxidized to their sulfates. The sulfates then are reduced to metallic nickel and cobalt by heating with hydrogen at elevated temperatures under pressure. The metals are obtained in their powder form.
The more common carbonyl refining process involves reaction of crude nickel with carbon monoxide under pressure at 100°C to form nickel tetracarbonyl, Ni(CO)4. The liquid tetracarbonyl upon heating at 300°C decomposes to nickel metal and carbon monoxide. Very pure nickel can be obtained by the carbonyl refining processes, as no other metal forms a similar carbonyl under these conditions.
| | Reactions | At ordinary temperatures, bulk nickel in compact form has no perceptible reactivity with air or water. However, in finely-divided state, the metal reacts readily and can be pyrophoric under certain conditions. When heated in air at 400°C or with steam, nickel converts to its oxide, NiO.
When heated with bromine vapors or chlorine gas, nickel catches fire forming nickel bromide, NiBr2, and yellow nickel chloride, NiCl2, respectively. Finely divided nickel combines with carbon monoxide to form zero valent nickel tetracarbonyl, Ni(CO)4. The reaction occurs at 50°C and one atmosphere, although it is usually carried out at 200°C under high CO pressure between 100 to 400 atm for high yield of carbonyl, and to prevent product decomposition. Carbon monoxide at ordinary pressure may be passed over freshly reduced metal to form the tetracarbonyl.
Finely divided nickel absorbs a large volume of hydrogen at high temperatures. Even at ordinary temperatures, considerable occlusion of hydrogen occurs on to the metal surface and no definite composition of any hydride formed is known. The metal activates molecular hydrogen to its atomic state, contributing to its catalytic action in hydrogenation of unsaturated compounds.
Dilute mineral acids attack nickel to a varying extent. The metal dissolves readily in dilute nitric acid. Evaporation of the solution forms emerald green crystals of nickel nitrate hexahydrate, Ni(NO3)2•6H2O.
Actions of dilute hydrochloric and sulfuric acid on nickel are relatively slow: slower than on iron. Concentrated nitric acid passivates the metal, oxidizing it and forming a protective film on its surface which prevents any further reaction.
Nickel is stable in caustic alkalies. At moderate temperatures, it decomposes gaseous ammonia into hydrogen and nitrogen. Nickel combines with sulfur, phosphorus, carbon, arsenic, antimony, and aluminum at elevated temperatures. Fusion of nickel powder with molten sulfur yields nickel sulfide, NiS. Reaction with aluminum can be explosive at 1,300°C, forming nickelaluminum intermetallic products of varying compositions.
Nickel powder combines with carbon dioxide in ammonia solution forming nickel carbonate. Boiling the solution to expel ammonia precipitates pure carbonate, NiCO3.
Fine nickel powder reacts with sulfamic acid in hot aqueous solution under controlled conditions, forming nickel sulfamate tetrahydrate, Ni(SO3NH2)2•4H2O, used in electroplating baths.
| | Toxicity | Skin contact can cause dermatitis and a type of chronic eczema, known as “nickel itch”, caused by hypersensitivity reactions of nickel on the skin (Patnaik, P. 1999. A Comprehensive Guide to the Hazardous Properties of Chemical Substances, 2nd ed. pp. 621-622, New York: John Wiley & Sons.) Although oral toxicity of the metal is very low, ingestion may cause hyperglycemia and depression of the central nervous system. Chronic inhalation of nickel dust can cause lung and sinus cancers in humans. Nickel and certain of its compounds are listed by IARC under Group 2B carcinogens as “possibly carcinogenic to humans” (International Agency for Research on Cancer. 1990. IARC Monograph, Vol. 49: Geneva.)
| | Description | Nickel is a hard, silvery white, malleable metal chunk or grey powder. Nickel powder is pyrophoric – can ignite spontaneously. It may react violently with titanium, ammonium nitrate, potassium perchlorate, and hydrazoic acid. It is incompatible with acids, oxidising agents, and sulphur. The industrially important nickel compounds are nickel oxide (NiO), nickel acetate (Ni(C2H3O2), nickel carbonate (NiCO3), nickel carbonyl (Ni(CO)4), nickel subsulphide (NiS2), nickelocene (C5H5)2Ni, and nickel sulphate hexahydrate (NiSO4 · 6H2O).
Nickel compounds have been well established as human carcinogens. Investigations into the molecular mechanisms of nickel carcinogenesis have revealed that not all nickel compounds are equally carcinogenic: certain water-insoluble nickel compounds exhibit potent carcinogenic activity, whereas highly water-soluble nickel compounds exhibit less potency. The reason for the high carcinogenic activity of certain water-insoluble nickel compounds relates to their bioavailability and the ability of the nickel ions to enter cells and reach chromatin. The water-insoluble nickel compounds enter cells quite efficiently via phagocytic processes and subsequent intracellular dissolution. Nickel is classified as a borderline metal ion because it has both soft and hard metal properties and it can bind to sulphur, nitrogen, and oxygen groups. Nickel ions are very similar in structure and coordination properties to magnesium.
| | Chemical Properties | silver white, hard, malleable metal chunks or grey powder | | Chemical Properties | RANEY NICKEL is a hard, ductile, magnetic metal with a silver-white color.
| | Physical properties | Nickel metal does not exist freely in nature. Rather, it is located as compounds in ores ofvarying colors, ranging from reddish-brown rocks to greenish and yellowish deposits, andin copper ores. Once refined from its ore, the metallic nickel is a silver-white and hard butmalleable and ductile metal that can be worked hot or cold to fabricate many items. Nickel,located in group 10, and its close neighbor, copper, just to its right in group 11 of the periodictable, have two major differences. Nickel is a poor conductor of electricity, and copper is anexcellent conductor, and although copper is not magnetic, nickel is. Nickel’s melting point is1,455°C, its boiling point is 2,913°C, and its density is 8.912 g/cm3. | | Isotopes | There are 31 isotopes of nickel, ranging from Ni-48 to Ni-78. Five of these arestable, and the percentage of their contribution to the element’s natural existence onEarth are as follows: Ni-58 = 68.077%, Ni-60 = 26.223%, Ni-61 = 1.140%, Ni-62 =3.634%, and Ni 64 = 0.926%. All of the other 26 isotopes of nickel are artificially madeand radioactive with half-lives ranging from a few nanoseconds to 7.6×104 years. | | Origin of Name | The name is derived from the ore niccolite, meaning “Old Nick,”
referred to as the devil by German miners. The niccolite mineral ore was also called
“kupfernickel,” which in German stands for two things; first, it is the name of a gnome
(similar to Cobalt), and second, it refers to “Old Nick’s false copper.” | | Occurrence | Nickel is the 23rd most abundant element found in the Earth’s crust. It is somewhat plentiful but scattered and makes up one-hundredth of 1% of igneous rocks. Nickel metal is foundin meteorites (as are some other elements). It is believed that molten nickel, along with iron,makes up the central sphere that forms the core of the Earth.There are several types of nickel ores. One is the major ore for nickel called pentlandite(NiS ? 2FeS), which is iron/nickel sulfide. Another is a mineral called niccolite (NiAs), discovered in 1751 and first found in a mining area of Sweden. By far, the largest mining area fornickel is located in Ontario, Canada, where it is recovered from what is thought to be a verylarge meteorite that crashed into the Earth eons ago. This large nickel deposit is one reasonfor the theory of the Earth’s core being molten nickel and iron, given that both the Earth andmeteorites were formed during the early stages of the solar system. Some nickel ores are alsofound in Cuba, the Dominican Republic, and Scandinavia. Traces of nickel exist in soils, coal,plants, and animals. | | Characteristics | As mentioned, nickel is located in group 10 (VIII) and is the third element in the specialtriad (Fe, Co, Ni) of the first series of the transition elements. Nickel’s chemical and physicalproperties, particularly its magnetic peculiarity, are similar to iron and cobalt.Some acids will attack nickel, but it offers excellent protection from corrosion from air andseawater. This quality makes it excellent for electroplating other metals to form a protectivecoating. Nickel is also an excellent alloy metal, particularly with iron, for making stainless steelas well as a protective armor for military vehicles. It is malleable and can be drawn throughdies to form wires. About one pound of nickel metal can be drawn to about 200 miles of thinwire. | | History | Discovered by Cronstedt in 1751 in kupfernickel (niccolite).
Nickel is found as a constituent in most meteorites and often
serves as one of the criteria for distinguishing a meteorite
from other minerals. Iron meteorites, or siderites, may contain
iron alloyed with from 5 to nearly 20% nickel. Nickel is
obtained commercially from pentlandite and pyrrhotite of the
Sudbury region of Ontario, a district that produces much of
the world’s nickel. It is now thought that the Sudbury deposit
is the result of an ancient meteorite impact. Large deposits
of nickel, cobalt, and copper have recently been developed at
Voisey’s Bay, Labrador. Other deposits of nickel are found in
Russia, New Caledonia, Australia, Cuba, Indonesia, and elsewhere.
Nickel is silvery white and takes on a high polish. It is
hard, malleable, ductile, somewhat ferromagnetic, and a fair
conductor of heat and electricity. It belongs to the iron-cobalt
group of metals and is chiefly valuable for the alloys it forms. It
is extensively used for making stainless steel and other corrosion-
resistant alloys such as Invar?, Monel?, Inconel?, and the
Hastelloys?. Tubing made of a copper-nickel alloy is extensively
used in making desalination plants for converting sea water
into fresh water. Nickel is also now used extensively in coinage
and in making nickel steel for armor plate and burglar-proof
vaults, and is a component in Nichrome?, Permalloy?, and
constantan. Nickel added to glass gives a green color. Nickel
plating is often used to provide a protective coating for other
metals, and finely divided nickel is a catalyst for hydrogenating
vegetable oils. It is also used in ceramics, in the manufacture
of Alnico magnets, and in batteries. The sulfate and the oxides are important compounds. Natural nickel is a mixture
of five stable isotopes; twenty-five other unstable isotopes are
known. Nickel sulfide fume and dust, as well as other nickel
compounds, are carcinogens. Nickel metal (99.9%) is priced at
about $2/g or less in larger quantities. | | Uses | The most common use of nickel is as an alloy metal with iron and steel to make stainlesssteel, which contains from 5% to 15% nickel. The higher the percentage of nickel in stainlesssteel, the greater the steel’s resistance to corrosion—particularly when exposed to seawater.Nickel is also alloyed with copper to make Monel metal, which was widely used before stainless steel became more economical and practical. It was used for many purposes as varied ashousehold appliances and general manufacturing. Nickel is also used to electroplate othermetals to provide a noncorrosive protective and attractive finish.
| | Uses | Nickel is used in various alloys, such asGerman silver, Monel, and nickel–chrome;for coins; in storage batteries; in spark plugs;and as a hydrogenation catalyst. | | Uses | Nickel-plating; for various alloys such as new silver, Chinese silver, German silver; for coins, electrotypes, storage batteries; magnets, lightning-rod tips, electrical contacts and electrodes, spark plugs, machinery parts; catalyst for hydrogenation of oils and other organic substances. See also Raney nickel. manufacture of Monel metal, stainless steels, heat resistant steels, heat and corrosion resistant alloys, nickel-chrome resistance wire; in alloys for electronic and space applications. | | Definition | ChEBI: Chemical element (nickel group element atom) with atomic number 28. | | Preparation | The carbonyl process is most commonly employed when very pure nickel is required.
The impure metal is reacted with pure carbon monoxide at 50° and the carbonyl produced
fractionated several times prior to pyrolysis at around 200°. The nickel thus obtained
has a purity of 99.90-99.99% depending upon the materials used.
Electrolytic methods for producing high purity nickel depend upon the production of high purity nickel salts. The nickel obtained by the electrolysis of pure nickel chloride solution with inert platinum-iridium anodes is 99.99% pure. | | Production Methods | Nickel is obtained by processing sulfide and laterite ore
concentrates using pyrometallurgic and hydrometallurgic
processes. The resultant nickel matte obtained by roasting
and smelting is subjected to further cleaning by electro-,
vapo-, and hydrometallurgic refining methods. Some portion
of the matte is roasted to obtain commercial nickel oxide
agglomerate. Pure, 99.9% nickel can be obtained by electrolytic
refining process.
The most pure, 99.97%, nickel is obtained by vapometallurgy.
In this process, known also as the Mond method,nickel and copper sulfide blend is converted to oxides and
then reduced by heating with water gas at 350–400°C. The
resultant active form of nickel is treated with carbon monoxide
to give volatile nickel carbonyl [Ni(CO)4]. The latter
reaction is reversible; heating results in pure nickel and
carbon monoxide. | | Definition | nickel: Symbol Ni. A malleable ductilesilvery metallic transition element;a.n. 28; r.a.m. 58.70; r.d. 8.9;m.p. 1450°C; b.p. 2732°C. It is foundin the minerals pentlandite (NiS),pyrrhoite ((Fe,Ni)S), and garnierite((Ni,Mg)6(OH)6Si4O11.H2O). Nickel isalso present in certain iron meteorites(up to 20%). The metal isextracted by roasting the ore to givethe oxide, followed by reductionwith carbon monoxide and purificationby the Mond process. Alternativelyelectolysis is used. Nickel metalis used in special steels, in Invar, and,being ferromagnetic, in magnetic alloys,such as Mumetal. It is also aneffective catalyst, particularly for hydrogenation reactions (see also raneynickel). The main compounds areformed with nickel in the +2 oxidationstate; the +3 state also exists (e.g.the black oxide, Ni2O3). Nickel wasdiscovered by Axel Cronstedt(1722–65) in 1751. | | Definition | A transition metal that occurs
naturally as the sulfide and silicate. It
is extracted by the Mond process, which involves
reduction of nickel oxide using carbon
monoxide followed by the formation
and subsequent decomposition of volatile
nickel carbonyl. Nickel is used as a catalyst
in the hydrogenation of alkenes, e.g. margarine
manufacture, and in coinage alloys.
Its main oxidation state is +2 and these
compounds are usually green.
Symbol: Ni; m.p. 1453°C; b.p. 2732°C;
r.d. 8.902 (25°C); p.n. 28; r.a.m. 58.6934. | | General Description | Nickel catalyst, is extremely fine powdered nickel. Nickel is grayish colored. Insoluble in water. Nickel catalyst is used to promote the chemical action in manufacturing synthetics and to process vegetable oil and petroleum. If exposed to air or moisture, Nickel may become hot enough to ignite. Nickel is insoluble in water and does not react with larger volumes of water. | | Air & Water Reactions | Pyrophoric, Ignites spontaneously in the presence of air; during storage, H2 escapes with fire and explosion hazards; reacts violently with acids forming H2. [Handling Chemicals Safely 1980. p. 807]. | | Reactivity Profile | Metals, such as METAL CATALYST, are reducing agents and tend to react with oxidizing agents. Their reactivity is strongly influenced by their state of subdivision: in bulk they often resist chemical combination; in powdered form they may react very rapidly. Thus, as a bulk metal Nickel is somewhat unreactive, but finely divided material may be pyrophoric. The metal reacts exothermically with compounds having active hydrogen atoms (such as acids and water) to form flammable hydrogen gas and caustic products. The reactions are less vigorous than the similar reactions of alkali metals, but the released heat can still ignite the released hydrogen. Materials in this group may react with azo/diazo compounds to form explosive products. These metals and the products of their corrosion by air and water can catalyze polymerization reactions in several classes of organic compounds; these polymerizations sometimes proceed rapidly or even explosively. Some metals in this group form explosive products with halogenated hydrocarbons. Can react explosively with oxidizing materials. | | Hazard | Nickel dust and powder are flammable. Most nickel compounds, particularly the salts, aretoxic. NiSO4 is a known carcinogen.
Although nickel is not easily absorbed in the digestive system, it can cause toxic reactionsand is a confirmed carcinogen in high concentration in the body. Nickel workers can receivesevere skin rashes and lung cancer from exposure to nickel dust and vapors.
Nickel is stored in the brain, spinal cord, lungs, and heart. It can cause coughs, shortnessof breath, dizziness, nausea, vomiting, and general weakness. | | Health Hazard | Ingestion of nickel can cause hyperglycemia,depression of the central nervous system,myocardial weakness, and kidney damage.A subcutaneous lethal dose in rabbits isin the range 10 mg/kg. The oral toxicityof the metal, however, is very low. Skincontact can lead to dermatitis and “nickelitch,” a chronic eczema, caused by dermalhypersensitivity reactions. Nickel itch mayresult from wearing pierced earrings. Inhalationof metal dusts can produce irritation ofthe nose and respiratory tract. Nickel andsome of its compounds have been reportedto cause lung cancer in experimental animals.It may also induce cancer in nose,stomach, and possibly the kidney. The experimentaldata on the latter, are not fully confirmative.Nickel refinery flue dust, nickelsulfide (Ni3S2) , and nickeloxide (NiO) produced localizedtumors in experimental animals wheninjected intramuscularly. IARC has classifiednickel and its compounds as carcinogenicto humans (IARC 1990). Inhalation ofmetal dusts can produce lung and sinus cancersin humans, with a latent period of about25 years.
Nickel is susceptible to cross human placentaand produce teratogenesis and embroytoxicity. In vitro study on lipid peroxidationindicated that nickel induced peroxidativedamage to placental membrane causing decreased placental viability, altered permeabilityand subsequent embroy toxicity (Chenand Lin 1998). In a latter study, Chen et al.(2003) evaluated nickel-induced oxidativestress and effects of antioxidants in humanlymphocytes. The levels of intracellular reactiveoxygen species, lipid peroxidation andhydroxyl radicals were examined for one hourfollowing acute treatment with Nicl2. Thestudy showed that glutathione, catalase andmannitol each provided protection against theoxidative stress induced by Ni.
The efficacy of organic chelating ligandsin cleaning human skin contaminated withnickel has been investigated (Healy et al.1998). Commercial liquid soap added withL-histidine was found to be more effectivethan the untreated soap. Similarly sodiumethylenediamine tetraacetic acid (EDTA)salt or L-histidine added to phosphate buffersaline solution was more effective in cleaningnickel contaminated human skin than thephosphate saline alone.
| | Fire Hazard | Flammable/combustible material. May ignite on contact with moist air or moisture. May burn rapidly with flare-burning effect. Some react vigorously or explosively on contact with water. Some may decompose explosively when heated or involved in a fire. May re-ignite after fire is extinguished. Runoff may create fire or explosion hazard. Containers may explode when heated. | | Agricultural Uses | Nickel (Ni) is a silver-white, ductile, malleable, yet
tough metallic element of Group 10 (formerly Group
VIII) of the Periodic Table. Mostly, nickel
goes into the making of steel and other corrosion resistant
alloys. Finely divided nickel is used as a hydrogenation
catalyst. Nickel is a beneficial trace element for plants.
Its presence in the urease enzyme underlines its
importance as a functional element. It is essential for
grain viability, in barley and at concentrations less than
100 μg/kg, the grain level and the germination frequency
decrease progressively. The quantity of Ni in a few
fertilizers is as given: 2 ppm in nitrochalk, 13 ppm in
superphosphate and 10 ppm in FYM.
Nickel is the metal component of urease that
hydrolyzes urea to give ammonia and carbon dioxide.
Compounds that react with nickel in the urease molecule
inhibit the hydrolysis of urea.
Nickel enhances the nodule weight and the seed yield
of soybeans, chickpeas and temperate cereals. It is
present in plants in the range of 0.1 to 1O ppm of the dry
weight.
High levels of Ni may induce Zn or Fe deficiency
because of cation competition, and may create nickel
toxicity. The browning and necrosis of the leaf tips and
margins are the toxicity symptoms on the plant. High Ni
content also causes the distortion of young leaves and the
death of the terminal shoots of the plant. The emerging
leaves may fail to unroll and become necrotic, with the
necrosis starting from near the base and spreading toward
the leaf tip. Nickel toxicity in cereals and grasses varies
in the intensity of chlorosis along the length of the leaf
with a series of transverse bands.
Sewage sludge contains heavy metals like Ni, Cd, etc.
that are absorbed by plants grown in soils contaminated
with these heavy metals. The toxicity caused by these
metals is in turn, passed on to animals that feed on such
plants. Any regulation for sludge use should ensure that
the soil pH is not lower than 6.5, as heavy metals are
insoluble at pH greater than 6.5. | | Safety Profile | Confirmed carcinogen
with experimental carcinogenic,
neoplastigenic, and tumorigenic data. Poison
by ingestion, intratracheal, intraperitoneal,
subcutaneous, and intravenous routes. An
experimental teratogen. Ingestion of soluble
salts causes nausea, vomiting, and diarrhea.
Mutation data reported. Hypersensitivity to
nickel is common and can cause allergic
contact dermatitis, pulmonary asthma,
conjunctivitis, and inflammatory reactions
around nickel-containing medcal implants
and prostheses. Powders may ignite
spontaneously in air. Reacts violently with
F2, NH4NO3, hydrazine, NH3, (H2 +
dioxane), performic acid, P, Se, S, (Ti +
KCLO3). Incompatible with oxidants (e.g.,
bromine pentafluoride, peroxyformic acid,
potassium perchlorate, chlorine, nitryl
fluoride, ammonium nitrate), Raney-nickel
catalysts may initiate hazardous reactions
with ethylene + aluminum chloride, pdioxane,
hydrogen, hydrogen + oxygen,
magnesium silicate, methanol, organic
solvents + heat, sulfur compounds. Nickel
catalysts have caused many industrial
accidents. | | Potential Exposure | Nickel is used as an alloy additive in
steel manufacture; in the production of coins and other
utensils. Nickel forms alloys with copper, manganese, zinc,
chromium, iron, molybdenum, etc. Stainless steel is the
most widely used nickel alloy. An important nickel copper
alloy is Monel metal, which contains 66% nickel and 32%
copper and has excellent corrosion resistance properties.
Permanent magnets are alloys chiefly of nickel, cobalt, aluminum,
and iron. Elemental nickel is used in electroplating,
anodizing aluminum casting operations for machine parts;
and in coinage; in the manufacture of acid-resisting and
magnetic alloys; magnetic tapes; surgical and dental instruments;
nickel cadmium batteries; nickel soaps in crankcase
oil; in ground-coat enamels; colored ceramics; and
glass. It is used as a catalyst in the hydrogenation synthesis
of acrylic esters for plastics. Exposure to nickel may also
occur during mining, smelting, and refining operations. The
route by which most people in the general population
receive the largest portion of daily nickel intake is through
food. Based on the available data from composite diet analysis,
between 300 and 600 μg nickel per day are ingested.
Fecal nickel analysis, a more accurate measure of dietary
nickel intake, suggests about 300 μg per day. The highest
level of nickel observed in water was 75 μg/L. Average drinking water levels are about 5 μg/L. A typical consumption
of 2 L daily would yield an additional 10 μg of nickel,
of which up to 1 μg would be absorbed. | | Carcinogenicity | Metallic nickel is reasonably anticipated to be a human carcinogenbased on sufficient evidence of carcinogenicity from studies in experimental animals. | | Environmental Fate | Nickel and its compounds are naturally present in the Earth’s
crust, and nickel can be released into the atmosphere via
natural discharges such as windblown dust and volcanic
eruptions. It is estimated that 8.5 million kilograms of nickel
are emitted into the atmosphere from natural sources such
as windblown dust, volcanoes, and vegetation each year.
Anthropogenic activities constitute significant discharge into
the environment, particularly in the form of particulate matter
and nickel compounds not normally found naturally; these
sources comprise five times the quantity estimated to come
from natural sources.
Nickel releases are mainly in the form of aerosols that cover
a broad spectrum of sizes. Particulates from power plants tend
to be associated with smaller particles than those from
smelters. Atmospheric aerosols are removed by gravitational
settling and dry and wet deposition. Submicrometer particles
may have atmospheric half-lives as long as 30 days. Monitoring
data confirm that nickel can be transported far from its source,
and that the form of nickel emitted to the atmosphere will vary
according to the type of source. Species associated with
combustion, incineration, and metals smelting and refining are
often complex nickel oxides, nickel sulfate, metallic nickel, and
in more specialized industries, nickel silicate, nickel subsulfide,
and nickel chloride.
Nickel may be transported into streams and waterways from
the natural weathering of soil as well as from anthropogenic
discharges and runoff. This nickel can accumulate in sediment,
with the adsorption of the metal to the soil depending on pH,
redox potential, ionic strength of the water, concentration of
complexing ions, and the metal concentration and type.
Soluble nickel compounds such as nickel chloride would be
expected to release divalent nickel into moist environments.
Since these compounds quickly dissolve upon exposure to
water, and partially due to the ubiquity of nickel in soil, water,
and air, tracking the course of these compounds through the
environment is difficult. This is particularly due to nickel’s
ability to complex with anionic species other than chloride to
form nickel oxide, sulfate, nitrate, carbonate, or acetate, among
others.
Industrial uses of nickel result in nickel being distributed
mainly at soil surfaces and through surrounding waterways and
water tables. Once distributed to the soil, nickel(II) ions can
potentially form inorganic crystalline minerals or precipitates,
can complex or adsorb onto organic and inorganic surfaces, can
participate in cation exchange, and can exist as free-ion or
chelated metal complexes in soil solution. | | Shipping | UN3089 Metal powders, flammable, n.o.s.,
Hazard Class: 4.1; Labels: 4.1-Flammable solid. UN3077
Environmentally hazardous substances, solid, n.o.s., Hazard
Class: 9; Labels: 9-Miscellaneous hazardous material,
Technical Name Required. | | Toxicity evaluation | Skin sensitization is believed to occur as a result of nickel
binding to proteins (particularly on the cell surface) and
hapten formation. The nickel–protein complex is recognized as
foreign and an immune reaction follows. For example, sweat
may react with the nickel in plated jewelry that comes in direct
contact with skin; dissolved metal may penetrate and react with
proteins in the skin, leading to immune sensitization. Nickel
may substitute for certain other metals (especially zinc) in
metal-dependent enzymes, leading to altered protein function.
High nickel content in serum and tissue may interfere with
both copper and zinc metabolism. It also readily crosses the cell
membrane via calcium channels and competes with calcium
for specific receptors.
Nickel can alter the sodium balance and lipid metabolism
and can induce metallothionein synthesis. Dissolved nickel
also affects the T-cell system and suppresses the activity of
natural killer cells. If given orally or by inhalation, nickel
chloride has been reported to decrease iodine uptake by the
thyroid gland. The lipid peroxidation properties of nickel can
introduce potential malignancies in humans, as DNA strand
gaps and breaks in DNA–protein cross-links can form. The
down-regulation of glycoprotein metabolism by nickel ions
may produce nephrotoxicity in humans as well. Nickel
carbonyl can cross-link amino acids to DNA and lead to
formation of reactive oxygen species. Nickel carbonyl can also
suppress natural killer cell activity and production of some
interferons.
Responses in many of these assays were weak and occurred
at toxic doses, and were affected by tissue culture conditions
modifying uptake by the cell. The mechanism of nickel carcinogenesis
is controversial, and is likely to vary with the form of
nickel. The nickel ion (Ni2+) alone does not form premutagenic
DNA lesions, suggesting that nickel causes indirect DNA
damage, perhaps due to oxidative stress or blocking DNA repair
mechanisms.
Nickel is an essential trace nutrient in plants and certain
animal species (e.g., rat and chick); however, it has not been
shown to be essential in humans. | | Incompatibilities | Nickel dust is a spontaneously flammable
solid and a dangerous fire hazard. | | Waste Disposal | Nickel compoundsencapsulation
followed by disposal in a chemical waste
landfill. However, nickel from various industrial wastes
may also be recovered and recycled as described in the
literature. |
| | Nickel Preparation Products And Raw materials |
| Raw materials | Sulfuric acid-->Sodium carbonate | | Preparation Products | 4-CHLORO-6-HYDRAZINO-PYRIMIDIN-5-YLAMINE-->6-Aminoindole-->4-AMINO-5-AMINOMETHYL-2-METHYLPYRIMIDINE-->4-AMINO-6-CHLOROPYRIMIDIN-5-YLAMINE-->1,2,4-Butanetriol-->secondary hydrocarbon steam reforming catalysts-->Benalaxyl-->5-AMINOPYRIMIDINE-->5-AMINO-6-CHLORO-PYRIMIDIN-4-OL-->4-AMINO-2-(TRIFLUOROMETHYL)PYRIMIDINE-5-CARBALDEHYDE-->1,4-Bis(3-aminopropyl)piperazine-->2-CHLORO-4,5-DIAMINOPYRIMIDINE-->Nickel oxide-->4-METHYLINDOLE-3-CARBOXALDEHYDE-->8-METHOXYQUINOLIN-6-AMINE-->(1-METHYL-4-PIPERIDINYL)METHANAMINE-->3-N-PENTADECYLPHENOL-->CYCLODODECANE-->Methyl 4-amino-3-methylbenzoate-->4,5-Dichloro-1,2-benzenediamine-->1,7-DIDEAZAADENINE-->6-AMINO-2-METHYL-2-HEPTANOL-->5-Chloroindole-3-carboxaldehyde-->methanation catalysts-->2,5-Dimethyl-2,5-hexanediol-->3-Phenylpropionic acid-->sec-Butylamine-->1,2-DIAMINO-2-METHYLPROPANE-->3-Hydroxy-1-methylpiperidine-->1-METHYL-PIPERIDINE-4-CARBONITRILE-->ISOPROPYL 4-AMINOBENZOATE-->Hydrogenated castor oil-->2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane-->N-Ethylpropylamine-->3-CARBETHOXY-2-PIPERIDONE-->N-(3-Aminopropyl)-imidazole-->NICKEL NITRATE-->Erythritol-->NICKEL(II) CARBONATE BASIC TETRAHYDRATE-->1,5-DIMETHYL-2-PYRROLIDINONE |
|